韩国lg化学一级代理商，价格电议。 特性： 无卤阻燃，中粘，脱模良好 应用： 电机，手机插头，电器配件 1301v-10 测试项目 测试方法 单位 数值 melt flow rate(300℃/1.2kg) astm d1238 g/10min 10 deity astm d792 1.2 mold shrinkage astm d955 mm/mm 0.005-0.007 water absorption@24h,23℃ astm d570 % 0.15 @equilibrium,50%rh,23℃ astm d570 % 0.32 refractive index,no astm d542 1.586 light tramittance astm d1003 % 89 haze astm d1003 % 0.7-1.5 deflection temperature under load(dtul)@4mm astm d648 ℃ @66 psi(0.45mpa),annealed astm d648 ℃ 144 @264 psi(1.8mpa),annealed astm d648 ℃ 141 @264 psi(1.8mpa),unannealed astm d648 ℃ 128 vicat softening point,50℃/hr,50n load astm d1525 ℃ 149 coefficient of linear thermal expaion,@-40 to 82℃ astm d696 mm/mm/℃ 68×10-6 teile yield strength astm d638 mpa 60 ultimate teile strength astm d638 mpa 71 elongation at yield astm d638 % 6 elongation at break astm d638 % 150 teile modulus astm d638 mpa 2410 flexural strength astm d790 mpa 96 flexural modulus astm d790 mpa 2410 notched izod impact @23℃ astm d256 j/m 900 unnotched izod impact @23℃ astm d256 no break itrumented dart impact,total energy @23℃ astm d3763 j 87 rockwell hardness astm d785 m scale 73 taber abrasion resistance (△haze) astm d1044 % 45 ul-94 @0.5mm astm d635 v-2 ul-94 @1.6mm astm d635 v-2 ul-94 @2.5-2.7mm astm d635 v-2 ul-94 @3.0mm astm d635 hb limiting oxygen index astm d2863 % 26 ball indentation temperature iec598-1 ℃ >125 average extent of burning astm d635 mm 25 gwt2.0mm,5second iec695-2-1 ℃ 850 comparative tracking index@2.0mm iec112 v 250 dielectric strength astm d149 kv/mm 17 eielectric cotant @60hz astm d150 3 dissipation factor@60hz astm d150 0.001 volume resistivity @23℃,dry astm d257 ω-cm 2.0×1017